General-purpose low-carbon steel wire. Heat treated. Without coating. Chemical composition, %: С=0.06-0.12, Si≤0.05, Mn=0.25-0.5, S≤0.05, P≤0.04. Breaking strength, Kgf: 290-490. General-purpose low-carbon steel wire. Not heat treated. Galvanized. Chemical composition, %: С=0.06-0.12, Si≤0.05, Mn=0.25-0.5, S≤0.05, P≤0.04. Breaking strength, kgf: 560-900. General-purpose low-carbon steel wire. Not heat treated. Chemical composition, %: С=0.06-0.12, Si≤0.05, Mn=0.25-0.5, S≤0.05, P≤0.04. Deviation from nominal diameter: Low carbon hot dipped steel wire. Heat-treated. Galvanized. Zinc coating: ≥ 40 gr/m2 Carbon content: 0.06-0.1% Tensile strength: 340-520 N/mm2 Common packing 20-70 kgs/coil Steel boiling. The absence of a wire rust, oxides, grease, after drawing. Coil with two ends (one-piece wire) Welding points should be treated (welding joint, processed core welding) 0.7mm +/- 0.05mm, 0.8mm +/- 0.05mm |